Properties

T est method

Test Value(ave.)

0.50mm

0.75 mm

1.00mm

1.25mm

1.50mm

2.00mm

2.50mm

Width(mm)

______

7000

7000

7000

7000

7000

7000

7000

Thickness -mm (min. ave.)

L owest individual of 10 values

ASTM D5199

nom.

-10%

nom.

-10%

nom.

-10%

nom.

-10%

nom.

-10%

nom.

-10%

nom.

-10%

Density g/cc(min.)

ASTM D1505/D792

0.940  

0.940

0.940

0.940

0.940

0.940

0.940

Tensile Properties:

Y ield strength

break strength

Y ield elongation

break elongation

ASTM D638

Type IV

10N/mm

16 N/mm

15%

780%

14N/mm

24 N/mm

15%

780%

19N/mm

33N/mm

15%

780%

24N/mm

41 N/mm

15%

780%

29N/mm

50N/mm

15%

780%

38N/mm

66 N/mm

15%

780%

46N/mm

83 N/mm

15%

780%

Tear 

Resistance-N

ASTM D1004

75

115

150

190

230

300

375

Puncture Resistance-N

ASTM D4833

240

360

480

590

680

840

950

Stress Crack Resistance

ASTM D5397(APP)

300hr.

300hr.

300hr.

300hr.

300hr.

300hr.

300hr.

Carbon Black Content-%

ASTM D1603 (3)

2.0-3.0%

2.0-3.0%

2.0-3.0%

2.0-3.0%

2.0-3.0%

2.0-3.0%

2.0-3.0%

Carbon Black Dispersion

ASTM D5596

note

note

note

note

note

note

note

Oxidative Induction Time(OIT) (min. ave.)

(a)Standard OIT 

or

(b)High Pressure OIT

ASTM D3895

ASTM D5885

100min.

400min.

100min.

400min.

100min.

400min.

100min.

400min.

100min.

400min.

100min.

400min.

100min.

400min.

Oven Age at 8 5

Standard OIT (min.ave.)-%retained after 90 days   

ASTM D5721

ASTM D3895

55%

55%

55%

55%

55%

55%

55%